Description: In production of Abrasion Resistant Plate, Martensite is a hard micro structural phase that is formed in steels by

Productkenmerken
Leveringscapaciteit en aanvullende infor...
Verpakking & Levering
Productoverzicht
Draag plaatplant
Product certificatie
FAQ op HP Wear -producten

Productkenmerken

Model: HP 700

merk: HP-plaat, HP-lassen

Standaard-: AiSi, ASTM, bs, DIN, GB, JIS

Plaats Van Herkomst: China

Soorten: Stalen plaat

Productieproces: Koudgewalst

Oppervlakte Behandeling: Gecoat

Toepassing: Flensplaat

Speciaal Staal: Slijtvast staal, Stalen plaat met hoge weerstand

Tolerantie: ± 1%

Categorie: Koudgewalste staalplaat, Thermisch verzinkte staalplaat, Laaggelegeerde plaat, Kleur gecoate staalplaat, Warmgewalste staalplaat, Stalen plaat

Verwerkingsservice: Buigen, Lassen, Decoiling, Snijden, Ponsen

Standard Thickness 3: 9on8, 12on8, 15on10,17on12, 20on12, 25on10

Standard Thickness 1: 3on5, 4on6, 6on6, 7on8, 8on8, 9on10, 10o

Standard Size 1: 3.9' X 4.8' Or 1200 X 2400mm

Standard Size 2: 7.2' X 9.9' Or 2200 X 3000mm

Leveringscapaciteit en aanvullende infor...

verpakkingen: Stalen frame en stalen riem bevestigd

produktiviteit: 500 tons per year

vervoer: Ocean,Land,Air,Express

Plaats van herkomst: China

Ondersteuning over: 50,000㎡ wear plate per year

Certificaat: ISO9001: 2015

GS-code: 72109000000

Haven: Shanghai,Qingdao,Shenzhen

betaling Type: L/C,T/T,D/P,Paypal

Incoterm: FOB,CFR,CIF,EXW,FCA,DDP,DDU,CPT,CIP

Verpakking & Levering

Verkoopeenheden:

Kilogram

Pakkettype:

Stalen frame en stalen riem bevestigd

Afbeeldingsvoorbeeld:

Download

The file is encrypted. Please fill in the following information to continue accessing it



Slijtplaatapplicaties ~ Cement.mp4



HP_ Welding Rebuild 14S.mp4



In production of Abrasion Resistant Plate, Martensite is a hard micro structural phase that is formed in steels by rapid cooling. Since martensitic alloys are air-hardenable the cooling rate plays an important part in the final hardness. Faster cooling usually results in harder surfacing deposits of Duplex Wear Resistant Plate. Preheating of 250 °F (121 °C) to 600 °F (316 °C) is generally required when working with martensitic alloys. This is to avoid cracking in the alloy deposit of Smooth Hardfacing Wear Plate.

The application of Non Cracked Overlay Plate in the cement industry includes powder separator blades, impact discs, pipes, pump casings, mill linings, crusher parts, slag troughs, various chassis, vibrating screen plates, etc.

Quick View On P roduct

1. Product Name: HP Non Cracked Overlay Plate

2. Body Material: A36 Mild Steel + Chromium Carbide Overlay (Hardfacing)

3. Standard Size: 1200*2400mm; 1000*3000mm or Customised

5. Quality Standard: ASTM G65, AISI, ASTM, BS, DIN, GB, JIS

6. Applications: Cement Industry , Steel Mill, Mining Site, Coal Mine, Chemical Industry, Power Generation & Others

7. Certification: ISO9001, SGS, CTI, ROHS

Wear Resistant Plates

Zigzag Wear Resistant Plates

Smooth Surface Wear Plates

Standard Specifications of HP Wear Plate :

Packing & Delivery of Wear Plate

Packing Way: By Steel Tube, By Steel Belt, By Steel Pallet

Delivery Time: 20 days after order confirmation

Wear Plates Packages On Pallet

Wear Plates Packages

Wear Plates Delivery

Anti-abrasion Comparison_HP Plate vs Other Plate

bedrijfsinformatie

HP Plate (Huifeng Wear Resistant Industry Co., Ltd.) was founded in 1994, as the former Taiwan's Upking-Kurimoto Ltd., led by president Mr. Zhang Kun-Mou, using the world-famous Japanese KURIMOTO hardfacing welding patented technology & welding materials produced by Vautid GmbH. HP Plate has become the most experienced expert specializing in production and sales of wear resistant products.

Wear Plate Production

HP Wear Products Range:

Abrasion Resistant Steel Plates (2)

HP Wear Product Applications

Cement Plant, Mining Site, Steel Mill, Power Generation, Glass Industry,

Dredging, Surgar Industy, Quarry, Construction, etc...where need to be anti-abrasion.

HP Factory Laboratory

Company ISO Certificates:

FAQ On HP Wear Products

Question: Can I cut or drill a hole in an HP overlay plate?

Answer: No. The chromium-carbide layer is not drillable or machineable. When necessary, you may be able to cut it with plasma, waterjet, or arc-gouging.

Question: Is it normal to see cracking in hardfacing plating?

Answer: It depends on the hardfacing alloy. Many chromium carbide alloys check-crack when cooled to moderate temperatures; dit is normaal. Other alloys, such as the austenitic and martensitic, do not crack when applied properly. Check cracking can be seen as cracking perpendicular to the bead length. This occurs by the high stress that is experienced when the weld metal cools. The cracking stops at the parent metal underneath, as long as the parent metal is not brittle. If the parent metal is hard or brittle, you should choose a buffer layer of a softer, and tougher, weld metal.

Question: What are the most popular applications with hardfacing products?

Antwoord: The typical applications include Mining Site, Steel Mill, Cement Industry, Power Generation, Glass Industry, Construction, Dredging, Oilsand, etc where need to fight with abrasion and impact.

Question: What metals can be protected with hardfacing?

Answer: Carbon and low-alloy steels with carbon contents of less than 1 percent can be hardfaced. High-carbon alloys may require a special buffer layer. Some of the base metals that can be hardfaced include: stainless steels, manganese steels, cast irons and steels, nickel-base alloys, copper-base alloys.

Question: What is hardfacing?

Answer: Hardfacing is also known as hardsurfacing. It is the process of adding wear-resistant weld metals to the surface of a metal part to protect it from wear and abrasion. Adding the weld metal plates can be achieved through welding or joining.

Productoverzicht

1. Productnaam: HP Chroom Carbide -overlay Slijtplaat

2. Lichaamsmateriaal: A36 Milde staal + chroomcarbide -overlay (hardfacing)

3. Grade: HP700, HP700S, HP750X, HP750P

4. Standaardgrootte: 1200*2400 mm; 1500*3000 mm; 2200*3000 mm of aangepast

5. Kwaliteitsnorm: ASTM G65, AISI, ASTM, BS, DIN, GB, JIS

6. Toepassingen: cementindustrie , staalfabriek, mijnbouwplaats, kolenmijn

Chemische industrie, stroomopwekking en anderen

7. Certificering: ISO9001, SGS, CTI, ROHS

Standaard specificaties van HP -slijtageplaat :

Verpakking en levering van slijtageplaat

Verpakkings manier: per stalen buis, per stalen riem, door stalen pallet

Levertijd: 20 dagen na bestelbevestiging

Prestatiecomparsie op verschillende slijtage van het type

HP Wear Products Bereik:

De typische toepassing van HP -slijtageplaat

@Mining -site

@Cem ent -industrie

Testfaciliteiten op HP -slijtageplaat

Metallografische foto's

@100x

@500X

HuiseG Wear Resistant Group is een professionele fabrikant die wordt toegewijd aan het aanbieden van slijtageproducten sinds 1989.
Wij leveren W -oordlaat, hardfacerende pijp, slijtagedelen, flux gekweekte lasdraad, slijtvast gietmateriaal en andere slijtage -oplossing.

We dienen al meer dan 30 jaar cementindustrie, mijnbouwplaats, energiecentrale, staalfabriek, glasindustrie, enz .... Als de grote mijlpaal tijdens onze groei heeft onze groep de joint venture opgezet met Vautid GmbH om de eerste klasse slijtageproducten in China te produceren. HP Group staat onder ISO9001 kwaliteitsbeheer en producten toegepast op SGS -certificering.

Draag plaatplant

Product certificatie

FAQ op HP Wear -producten

Vraag: Kan ik een gat in een HP -overlay -plaat snijden of boren?

Antwoorden: Nee. De chroom-carbide-laag is niet boorbaar of machinaal. Indien nodig kunt u het mogelijk snijden met plasma, waterjet of booggouging.

Vraag: Is het normaal om kraken te zien in hardfacing -plating?

Antwoorden: Het hangt af van de hardfacerende legering. Veel chroomcarbide-legeringen check-crack wanneer gekoeld tot matige temperaturen; dit is normaal. Andere legeringen, zoals de austenitische en martensitische, barsten niet wanneer ze correct worden aangebracht. Controleer kraken kan worden gezien als krakend loodrecht op de kralenlengte. Dit gebeurt door de hoge spanning die wordt ervaren wanneer het lasmetaal afkoelt. Het kraken stopt bij het onderliggende ouder metaal, zolang het oudermetaal niet bros is. Als het oudermetaal hard of bros is, moet u een bufferlaag kiezen van een zachter en strengere lasmetaal.

Vraag: Wat zijn de meest populaire toepassingen met hardfacing -producten?

Antwoorden: De typische toepassingen zijn onder meer mijnbouwplaats, staalfabriek, cementindustrie, stroomopwekking, glasindustrie, constructie, baggeren, oliën en enz. Waar nodig om te vechten met slijtage en impact.

Vraag: Welke metalen kunnen worden beschermd met hardfacing?

Antwoorden: Koolstof en staal met lage legering met koolstofgehalten van minder dan 1 procent kan hard worden. Koolstoflegeringen vereisen mogelijk een speciale bufferlaag. Sommige van de basismetalen die hard kunnen worden gevormd, zijn: roestvrij staal, mangaanstaals, gegoten ijzers en staalsoorten, legeringen van nikkelbasis, koperbasislegeringen.

Vraag: Wat is hardfacing?

Antwoorden: Hardfacing staat ook bekend als hardsurfacing. Het is het proces van het toevoegen van slijtvaste lasmetalen aan het oppervlak van een metalen deel om het te beschermen tegen slijtage en slijtage. Het toevoegen van de lasmetaalplaten kan worden bereikt door lassen of samenvoegen.

Chromiumcarbide hardfaceplaat